Abstract In this work, an equi-atomic AlCrFeMnNiV HEA was synthesized by means of arc-melting and casting processes. The casted alloy ingots were heat-treated (annealed) at temperatures of 400, 600 and 800 ºC, for 2 h. The effect of the heat-treatment temperature on the HEA microstructural evolution, compressive strength and corrosion behavior was investigated. Heat-treatment temperatures of 400 and 600 ºC resulted in increased micro-hardness properties that, at 800 ºC, were drastically reduced, although a good combination between strength and ductility was observed. HEA showed an extreme decrease in the current density (J (A/cm2)), after the heat-treatment, with a lower potential (V). The heat-treated HEA demonstrated a good corrosion rate in acidic conditions, as compared to that of nickel (Ni) based, titanium (Ti) alloys and stainless steel (SS) super alloys.

Abstract Ti10Fe5Si5Cr3Nb composite coatings were fabricated using laser cladding technique. Laser power was varied from 800W to 1200W while the scanning speed was kept constant at 1.5 m/min. The microstructural analysis of the samples was conducted by using optical microscope, X-ray diffractometer and scanning electron microscope coupled with energy dispersive spectroscopy. Potentiodynamic polarization and diamond indenter were used to study the corrosion and microhardness properties of the alloy. The alloy exhibited a dendritic microstructure with Si-rich dispersed phase. Grain coarsening was observed to be dependent on coating depth. The microhardness was high at the top and decreased with coating depth. No improvement in corrosion resistance was noticed but the presence of Cr in the alloy promoted passivation.